Spore Black & Spore Black E9 are inherently Anti-static, 100% powder-free premium quality ESD finger cots. The ESD property in Spore Black finger cots series will not weaken along the age. Surface resistivity at 106 – 108 ohms/square (Spore Black) and 109ohms/square (Spore Black E9) respectively, exceeds most of the ESD application requirements.Spore Black finger cots series are ESD & RoHS-certified. They do not contain heavy metal substances. 100% bio-degradable. Environmental friendly. An excellent finger cot to use in ESD & cleanroom environment.
Features
- Conductive agents are blended with latex to provide consistent ESD performance.
- Suitable for handling ESD sensitive components or assemblies that require ani-static function.
- Special washing process to reduce ionics, non-volatile residue, particles and other contaminants.
Area of Use (productions)
- High ESD production environment
- Memory chip production
- Micro electrical components
- High presicion metal components assembly
- Semi-conductors
- Disk drive / thin film heads
- Computer hard disk production
- Watch manufacturing
- Cleaning and handling of precision components
| Product | Spore Black Clean | Spore Black Chlorinated | Spore Black E9 Chlorinated | |
| Internal Diameter (mm) | S15.0 | 15 | 15 | 15 |
| M18.0 | 18 | 18 | 18 | |
| L21.0 | 21 | 21 | 21 | |
| XL24.0 | - | 24 (Smooth Surface Only) | - | |
| Thickness (mm) | 0.1 ± 0.02 | |||
| Length (mm) | 63 ± 2 | 63 ± 2 45 ± 2 (cut type only) |
63 ± 2 | |
| Physical Test (ASTM D412) Elongation Tensile Strength |
Min 700 % Min 30 Mpa |
|||
| Surface Resistivity (ASTM D257) | 106 ~ 108 Ohm/square | 109 Ohm/square | ||
| Surface Texture | Rough Surface only | Smooth & Rough Surface | Smooth only | |
| Type | Unroll/ Roll/ Cut | Unroll / Roll | Unroll / Roll | |
| Cut (only in Rough surface) | ||||
| Packaging (per carton) |
1440 pcs x 20 bags | 720 pcs x 40bags 1440 pcs x 20 bags |
1440 pcs x 20 bags | |
| Shelf Life (Recommendation) | Approximately 3 months | Approximately 9 months | ||
| Remarks |
|
|||